Brutus G Gas Brazing Alloy

SKU: RM-4102

For all ferrous and non-ferrous metals, exceptionally good for high strength joints (Except white metals). Brutus G produces the very highest strength thin joints for repairing machinery and equipment. This alloy has an excellent wetting action and is easy to use. Since no special preparation is necessary, Brutus G is ideal for the most difficult maintenance repair jobs where crack-free results are essential. Strongest joints are only .003 inches thick.

Brutus G can also be used to build up surfaces and its deposits will work harden, producing a low friction durable surface.  Download PDF

Features

Very High Strength 100,000 psi
Silver Content Aids Wetting
Low Melting Temperature
Durable Flux Coating

Very Thin Flowing
Work Hardens
Minimum Preparation
Easy To Machine Non-Peeling

Applications

Brutus G is ideal for the most difficult maintenance repair jobs where crack-free results are essential.
High strength repairs on everything from cast iron to stainless steel

Recommended Settings

Use Neutral Flame
Temperature: 1575°F (857°C)

Recommended Settings:
1/16 Diameter – 1.6 mm
3/32 Diameter – 2.4 mm
1/8 Diameter – 2.3 mm

Best Practices

Clean joint thoroughly.
For increased capillary action on butt or thin joints apply additional Brutus Flux (available separately).
Heat entire joint to dull red and continue heat until alloy penetrates.
Do not melt base metal.
To form bead, use low torch angles and apply alloy one drop at a time.